The L <-> Al + Al11Ce3 technologically important eutectic transformation in Al-Ce binary alloys, containing from 5 to 20 wt.% Ce and ranging from hypo- to...
This paper presents a study that aims to modify the interfacial characteristics of maraging steel-H13 bimetal structures through heat treatment procedures....
The distribution, morphology, and chemical composition of various k-phases present in the wire-arc additive manufactured (WAAM) nickel aluminum bronze (NAB) of...
As a step forward toward the development of the next generation of nickel aluminum bronze (NAB) components using wire-arc additive manufacturing (WAAM), square...
A comprehensive study was intended to show the microstructural features of additively manufactured (AM) 18Ni-300 maraging steel. Uniaxial tensile tests were...
Additive manufacturing of a low carbon Fe-Cr-Ni-Al maraging stainless steel (with the brand name CX) through the laser-powder bed fusion (LPBF) process is...
Instrumented indentation is a semi-destructive and robust technique to assess micromechanical characteristics (e.g., local properties) of metallic materials at...
Cylindrical rods of Ti-6Al-4V (Ti64) alloy were additively produced using the electron beam melting (EBM) process in the horizontal and vertical directions....
The effects of spark plasma sintering (SPS) coupled with hot upset forging of aluminum 2219 powder were studied. SPS was found to be an effective means of...
Canada Department of Mines and Technical Surveys, 1960
A circular feature 1.46 miles in diameter and 100 feet deep located at longitude 76° 38' W and latitude 44° 27' N in southeastem Ontario has been investigated...
Rapport
Texte intégral en ligne
Filtrer vos résultats
Opération réussie
L’élément a été sauvegardé.
Opération réussie
Cet élément a été retiré.
Erreur
Vous avez dépassé le nombre maximal de 100 résultats sauvegardés.
Erreur
Impossible de sauvegarder l’élément. Veuillez réessayer. Si le problème persiste, il pourrait y avoir un problème avec l’élément.
Erreur
Impossible de supprimer l’article demandé. Veuillez réessayer plus tard.